Backing/Carrier Siliconized Sponge
Adhesive Acrylic
Thickness 62.5 Mils
Adhesion
  Compare Now

512AF.063 is a 1/16 inch, modified cell, silicone fire blocking foam with a film supported acrylic adhesive. It offers superior service life, excellent conformability, and flexibility.

Backing/Carrier Siliconized Sponge
Adhesive Acrylic
Thickness 93.75 Mils
Adhesion
  Compare Now

512AF.094 is a 3/32 inch, modified cell, silicone fire blocking foam with a film supported acrylic adhesive. It offers superior service life, excellent conformability, and flexibility.

Backing/Carrier Siliconized Sponge
Adhesive Acrylic
Thickness 125 Mils
Adhesion
  Compare Now

512AF.125 is a 1/8 inch, modified cell, silicone fire blocking foam with a film supported acrylic adhesive. It offers superior service life, excellent conformability, and flexibility.

Backing/Carrier Siliconized Sponge
Adhesive Acrylic
Thickness 187.5 Mils
Adhesion
  Compare Now

512AF.1875 is a 3/16 inch, modified cell, silicone fire blocking foam with a film supported acrylic adhesive. It offers superior service life, excellent conformability, and flexibility.

Backing/Carrier Siliconized Sponge
Adhesive Acrylic
Thickness 250 Mils
Adhesion
  Compare Now

512AF.25 is a 1/4 inch, modified cell, silicone fire blocking foam with a film supported acrylic adhesive. It offers superior service life, excellent conformability, and flexibility.

Backing/Carrier Siliconized Sponge
Adhesive
Thickness
Adhesion oz/in
  Compare Now

Saint-Gobain NorSealĀ® r10480M silicone sponge rubber is a low compression set closed-cell sponge that can be used in most gasketing applications. This material is flexible and compressible and designed for use in extreme temperature ranges, with excellent weatherability, compression set resistance, electrical strength and non-stick properties.